In situ hydrothermal synthesis of visible light active sulfur doped TiO2 from industrial TiOSO4 solution
Hong Pu, Congxue Tian, Hui Zhang
Abstract
A cost-effective industrial TiOSO 4 solution was employed to fabricate visible light active sulfur-doped titanium dioxide (S-TiO 2 ) via a facile hydrothermal method. The effect of calcination temperature on morphology, particle size, crystallinity, and photocatalytic property of S-TiO 2 was systematically investigated. Successful incorporation of sulfur into TiO 2 was confirmed by carbon-sulfur analysis, X-ray photoelectron spectroscopy (XPS), and Energy dispersive spectrometer (EDS). The research results demonstrated that calcination temperature significantly impacted the crystallinity, specific surface area, sulfur content, and light absorption properties of S-TiO 2 . The catalyst calcined at 400 °C revealed the highest photocatalytic activity, with a rate constant of 0.02408 min −1 , approximately 25 times higher than commercial P25 catalyst. The higher activity was attributed to the synergistic effect of well-crystallized anatase phase, specific surface area, and red shift of spectral absorption.