Radiation effects of high-fluence reactor neutron on Ni/<b> <i>β</i> </b>-Ga2O3 Schottky barrier diodes
Leidang Zhou, Hao Chen, Tongling Xu, Jinlu Ruan, Yuru Lai, Yuxin Deng, Jiaxiang Chen, Xinbo Zou, Xing Lü, Liang Chen, Xiaoping Ouyang
Abstract
This study investigates the broad-energy-spectrum reactor-neutron irradiation effects on the electrical characteristics of Ni/β-Ga2O3 Schottky barrier diodes (SBDs), where the irradiated neutron fluence was up to 1 × 1016 cm−2. On the one hand, the high neutron fluence of 1016 cm−2 resulted in a reduction in forward current density by two orders of magnitude and an extremely high on-resistance property due to the radiation-generated considerable series resistance in the SBD. On the other hand, the irradiation brought little influence on the Ni/β-Ga2O3 Schottky contact, since the extracted ideality factor and barrier height from temperature-dependent current–voltage (I–V–T) characteristics showed no significant changes after the radiation. Moreover, the capacitance–voltage (C–V) characterization revealed that the net carrier density in the β-Ga2O3 material was only reduced by 25% at the neutron fluence of 1015 cm−2 but a significant reduction by 2–3 orders at 1016 cm−2. Within the neutron fluence range of 2 × 1014 cm−2 up to 1016 cm−2, the carrier removal rates trended to be saturated with the increased fluences, following an exponential regular. In addition, the C–V measurement on the 1016 cm−2 irradiated sample exhibited an obvious frequency dispersion, and the extracted carrier distribution was not uniform.