Low Threshold Quantum Dot Lasers Directly Grown on Unpatterned Quasi-Nominal (001) Si
Yating Wan, Chen Shang, Justin Norman, Bei Shi, Qiang Li, Noelle Collins, Mario Dumont, Kei May Lau, A. C. Gossard, John E. Bowers
Abstract
We report electrically pumped, continuous-wave (cw) InAs/GaAs quantum dot (QD) lasers directly grown on quasi-nominal Si (001) substrates with offcut angle as small as 0.4°. No GaP, Ge buffer layers or substrate patterning is required. An anti-phase boundary free epitaxial GaAs film was grown by metal-organic chemical vapor deposition (MOCVD) with a low threading dislocation density of 3 × 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">7</sup> cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-2</sup> . Room-temperature cw lasing at ~1.3 μm has been achieved, with a minimum threshold current density of 34.6 A/cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> per layer, a maximum operating temperature of 80 °C, and a maximum single facet output power of 52 mW. A comparison of various monolithic III-V hetero-epitaxy on Si solutions is presented. Direct growth on unpatterned quasi-nominal (001) Si may yield the best material quality at the lowest lifecycle cost.