Upscaling of LATP synthesis: Stoichiometric screening of phase purity and microstructure to ionic conductivity maps
Nikolas Schiffmann, Ethel C. Bucharsky, Karl G. Schell, Charlotte Fritsch, Michael Knapp, Michael J. Hoffmann
Abstract
Abstract Lithium aluminum titanium phosphate (LATP) is known to have a high Li-ion conductivity and is therefore a potential candidate as a solid electrolyte. Via sol-gel route, it is already possible to prepare the material at laboratory scale in high purity and with a maximum Li-ion conductivity in the order of 1·10 −3 s/cm at room temperature. However, for potential use in a commercial, battery-cell upscaling of the synthesis is required. As a first step towards this goal, we investigated whether the sol-gel route is tolerant against possible deviations in the concentration of the precursors. In order to establish a possible process window for sintering, the temperature interval from 800 °C to 1100 °C and holding times of 10 to 480 min were evaluated. The resulting phase compositions and crystal structures were examined by X-ray diffraction. Impedance spectroscopy was performed to determine the electrical properties. The microstructure of sintered pellets was analyzed by scanning electron microscopy and correlated to both density and ionic conductivity. It is shown that the initial concentration of the precursors strongly influences the formation of secondary phases like AlPO 4 and LiTiOPO 4 , which in turn have an influence on ionic conductivity, densification behavior, and microstructure evolution.