Effects of Transition Metals on the Electrical Conductivity of M-Doped MnCo<sub>2</sub>O<sub>4</sub> (M = Cu, Ni, Zn) as Contact Layer on Precoated SUS441 in Solid Oxide Cells
Hao Shi, Haozhen Li, Xing Zhou, Chongqing Yang, Hengyong Tu, Jun Tong, Longkai Xiang, Chao Ma, Lei Zhu, Zhen Huang
Abstract
Spinels have been widely employed as contact layers (CLs) on metallic interconnects for solid oxide cells (SOCs) with the required electrical conductivity and Cr block ability. In this work, MnCo 2 O 4 spinels doped with different transition metals (Cu, Ni, and Zn) were deposited on precoated SUS441 stainless steel as CLs. A positive doping effect of Cu and Ni on increasing the concentration of Mn 4+ /Mn 3+ and Co 3+ /Co 2+ hopping pairs was observed, whereas a negative doping effect of Zn on electrical conductivity was confirmed, which was reflected in the data of X-ray photoelectron spectroscopy (XPS) and X-ray absorption spectra (XAS). The Cu-doped Mn 1 Co 1.7 Cu 0.3 O 4 spinel exhibited the best electrical conductivity with a low area specific resistance (ASR) value of 4.5 mΩ·cm 2 at 850 °C. A relative degradation test demonstrated that Mn 1 Co 1.7 Cu 0.3 O 4 maintained significant performance during a 200 h isothermal process. Cross-sectional observations revealed that the thickness of the Cr oxide scale formed during the degradation test was much reduced by the Mn 1 Co 1.7 Cu 0.3 O 4 CL, which was attributed to the improved resistance to Cr oxidation. The present work shed light on the design of highly conductive CLs in SOCs.