Additive Engineering of the CuSCN Hole Transport Layer for High-Performance Perovskite Semitransparent Solar Cells
Jingsong Sun, Ningjun Zhang, Jiarui Wu, Weichuang Yang, Haiyan He, Mianji Huang, Yuheng Zeng, Xi Yang, Zhiqin Ying, Ganghua Qin, Chunhui Shou, Jiang Sheng, Jichun Ye
Abstract
CuSCN has been widely considered a promising candidate for low-cost and high-stable hole transport material in perovskite semitransparent solar cells (STSCs). However, the low conductivity of the solution-processed CuSCN hole transport layer (HTL) hinders the hole extraction and transport in devices, which makes it hard to achieve devices with high performance. Herein, we report a facile additive engineering approach to optimize the p conductivity of CuSCN HTLs in perovskite STSCs. The n-butylammonium iodide additive facilitates the formation of Cu2+ and generates more Cu vacancies in the CuSCN HTL. This realizes a significant enhancement of the hole concentration and p conductivity of the film. Moreover, the additive improves the solubility of the CuSCN precursor solution and results in a uniform coverage on the perovskite active layer. Therefore, the perovskite STSC with a high power conversion efficiency (PCE) of 19.24% has been achieved, which is higher than that of the spiro-OMeTAD (18.83%) and CuSCN (17.45%) counterparts. In addition, the unencapsulated CuSCN-based device retains 87.5% of the initial PCE after 20 days in the ambient atmosphere.