Origin of observed narrow bandgap of mica nanosheets
Shunnian Wu, W.P. Cathie Lee, Ping Wu
Abstract
Abstract Mica nanosheets possess peculiar feature of narrowed bandgap with the decrease of thickness but a conclusive theoretical understanding of the narrowing mechanisms is still under development. In this report, first-principles calculations were carried out to investigate the electronic band structure of mica nanosheets with the deposition of K 2 CO 3 . Bulk mica shows an indirect bandgap of 4.90 eV. Mica nanosheets show similar electronic structures to bulk mica with a gradually increased bandgap of 4.44 eV, 4.52 eV and 4.67 eV for 1-layer, 2-layers and 3-layers nanosheets, respectively, which is attributed to the lattice relaxation. K 2 CO 3 is found to have strong affinity towards mica nanosheets. The K 2 CO 3 deposited mica nanosheets showed an increased bandgap with the increase of thickness, consistent with experimental observations. The calculated bandgap of K 2 CO 3 deposited mica for 2-layers and 3-layers nanosheets are 2.60 eV and 2.75 eV, respectively, which are comparable with the corresponding experimental values of 2.5 eV and 3.0 eV. Our theoretical findings support the experimental evidence of surface contamination of mica by K 2 CO 3 , and provide new insight into the structure and properties of 2D mica.