Photoluminescence Properties of AScSi<sub>2</sub>O<sub>6</sub>:Cr<sup>3+</sup> (A = Na and Li) Phosphors with High Efficiency and Thermal Stability for Near-Infrared Phosphor-Converted Light-Emitting Diode Light Sources
Yan Yu, Mengmeng Shang, Shuai Huang, Yining Wang, Yixin Sun, Peipei Dang, Jun Lin
Abstract
Near-infrared (NIR) phosphors are fascinating photoluminescence materials with applications in phosphor-converted light-emitting diodes (pc-LEDs) for night vision lighting, which are still restricted by low efficiency and thermal stability in the current research stage. In this work, AScSi2O6 (A = Na/Li) are chosen as hosts due to a larger band gap and a single octahedral site for Cr3+ doping. The NIR-emitting Cr3+-activated AScSi2O6:Cr3+ phosphors were successfully prepared by a common high-temperature solid-state method. X-ray diffraction and Rietveld refinement confirm that the Cr3+ prefers to enter the Sc3+-octahedral lattice site in the AScSi2O6 structure. Under blue light excitation, AScSi2O6:Cr3+ phosphors exhibit broadband NIR emission from 700 to 1100 nm with a full width at half-maximum of ∼150 nm owing to the 4T2 → 4A2 electron transition of Cr3+. The photoluminescence properties were enhanced by adjusting the fluxes and sintering conditions, and highly efficient LiScSi2O6:Cr3+ NIR phosphors with external quantum efficiencies of 33.4% were obtained. Moreover, the optimized LiScSi2O6:Cr3+ exhibits excellent thermal stability (75% at 150 °C) with an activation energy of 0.33 eV. Importantly, the fabricated NIR pc-LED with the highly efficient LiScSi2O6:Cr3+ phosphor demonstrates brighter NIR light and a higher luminous efficacy than the NaScSi2O6:Cr3+ phosphor in night vision.