Ultrafine-Grained Tungsten Heavy Alloy Prepared by High-Pressure Spark Plasma Sintering
Shuaihao Zhang, Qiqi Zhu, Qiunan Li, Wei Ji, Weimin Wang, Zhengyi Fu
Abstract
Tungsten heavy alloy (WHA) is an ideal material employed for kinetic energy penetrators due to its high density and excellent mechanical properties. However, it is difficult to obtain ultrafine-grained tungsten alloy with excellent properties by traditional powder metallurgy method because of severe grain growth at a high sintering temperature with a long soaking time. In this study, the sintering behavior of tungsten alloys was studied at 800 to 1300 °C, and highly dense 93W-5.6Ni-1.4Fe (wt.%) WHA was successfully fabricated at a low temperature of 950 °C with a high pressure of 150 MPa by spark plasma sintering. The as-sintered tungsten alloy possesses a high relative density (98.6%), ultrafine grain size (271 nm) and high dislocation density (2.6 × 1016 m−2), which results in excellent properties such as a high hardness (1079 HV1). The high sintering pressure is considered to support an additional driving force for the sintering and lead to a low-temperature densification, which effectively limits grain growth.