Microstructure and mechanical properties of brazing joint of silver-based composite filler metal
Hua Yu, Liangliang Zhang, Fangfang Cai, Sujuan Zhong, Jia Ma, Li Bao, Yongtao Jiu, Bingli Hu, Shizhong Wei, Weimin Long
Abstract
Abstract In this article, environmental friendly BAg25Cu40Zn34Sn (BAg-25) and BAg30Cu37Zn32Sn (BAg-30) flux-core solder metal capable of facilitating automatic production of brazing manufacturing processes were prepared. The butt and lap induction brazing tests were carried out on the substrate with BAg-25 and BAg-30. Wettability, microstructure and mechanical properties of the solders on the base metal were studied by field emission scanning electron microscope (SEM-EDS), electron backscattering diffraction (EBSD), tensile testing machine and microhardness tester. Results indicated that the wetting property of BAg-30 with 30% silver content was better than that of BAg-25 with 25% silver content. At the same time, besides copper and silver-based solid solutions, the brazed joint of BAg-30 solder also contain Cu + Ag eutectic phase. In the brazed joint of BAg-25 solder, the grain size is smaller, which makes the tensile strength and the shear strength of the joints better. Therefore, the BAg-25 flux-core solder metal will further reduce the industrial cost and meet the requirements of mechanical properties.