Surface Coating Enabling Sulfide Solid Electrolytes with Excellent Air Stability and Lithium Compatibility
Min Luo, Changhong Wang, Yi Duan, Xuyang Zhao, Jiantao Wang, Xueliang Sun
Abstract
All‐solid‐state lithium metal batteries (ASSLMBs) featuring sulfide solid electrolytes (SEs) are recognized as the most promising next‐generation energy storage technology because of their exceptional safety and much‐improved energy density. However, lithium dendrite growth in sulfide SEs and their poor air stability have posed significant obstacles to the advancement of sulfide‐based ASSLMBs. Here, a thin layer (approximately 5 nm) of g‐C 3 N 4 is coated on the surface of a sulfide SE (Li 6 PS 5 Cl), which not only lowers the electronic conductivity of Li 6 PS 5 Cl but also achieves remarkable interface stability by facilitating the in situ formation of ion‐conductive Li 3 N at the Li/Li 6 PS 5 Cl interface. Additionally, the g‐C 3 N 4 coating on the surface can substantially reduce the formation of H 2 S when Li 6 PS 5 Cl is exposed to humid air. As a result, Li–Li symmetrical cells using g‐C 3 N 4 ‐coated Li 6 PS 5 Cl stably cycle for 1000 h with a current density of 0.2 mA cm −2 . ASSLMBs paired with LiNbO 3 ‐coated LiNi 0.6 Mn 0.2 Co 0.2 O 2 exhibit a capacity of 132.8 mAh g −1 at 0.1 C and a high‐capacity retention of 99.1% after 200 cycles. Furthermore, g‐C 3 N 4 ‐coated Li 6 PS 5 Cl effectively mitigates the self‐discharge behavior observed in ASSLMBs. This surface‐coating approach for sulfide solid electrolytes opens the door to the practical implementation of sulfide‐based ASSLMBs.