Pyrolysis Kinetics of Lignin-Based Flame Retardants Containing MOFs Structure for Epoxy Resins
Tianyu Yao, Ruohan Yang, Cong Sun, Yuzhu Lin, Ruoqi Liu, Hongyu Yang, Jiajia Chen, Xiaoli Gu
Abstract
This study describes the preparation of a lignin-based expandable flame retardant (Lignin-N-DOPO) using grafting melamine and covering 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) using the Mannich reaction. Then, through in situ growth, a metal-organic framework (MOF) HKUST-1 (e.g., Cu3(BTC)2, BTC = benzene-1,3,5-tricarboxylate)/lignin-based expandable flame retardant (F-lignin@HKUST-1) was created. Before that, lignin epoxy resin containing phosphorus (P) and nitrogen (N) components had been created by combining epoxy resin (EP) with F-lignin@HKUST-1. Thermogravimetric analysis was used to examine the thermal characteristics of epoxy resin (EP) composite. The findings indicate that the thermal stability of EP is significantly affected by the presence of F-lignin@HKUST-1. Last but not least, the activation energy (E) of EP/15% F-lignin@HKUST-1 was examined using four different techniques, including the Kissinger-SY iteration method, the Ozawa-SY iteration method, the Lee-Beck approximation-iteration method, and the Gorbatchev approximation-iteration method. It was discovered that the activation energy was significantly higher than that of lignin. Higher activation energy suggests that F-lignin@HKUST-1 pyrolysis requires more energy from the environment, which will be significant about the application of lignin-based flame retardants.