Na<sub>2</sub>B<sub>11</sub>H<sub>13</sub> and Na<sub>11</sub>(B<sub>11</sub>H<sub>14</sub>)<sub>3</sub>(B<sub>11</sub>H<sub>13</sub>)<sub>4</sub> as potential solid-state electrolytes for Na-ion batteries

Diego H. P. Souza, Anita M. D’Angelo, Terry D. Humphries, Craig E. Buckley, Mark Paskevicius

2022Dalton Transactions14 citationsDOI

Abstract

Na 2 B 11 H 13 and Na 11 (B 11 H 14 ) 3 (B 11 H 13 ) 4 exhibit ionic conductivity above 1 mS cm −1 at 100 °C and an electrochemical stability of 2.1 V vs. Na + /Na. Na 11 (B 11 H 14 ) 3 (B 11 H 13 ) 4 partially stabilises the high temeprature polymorph at 25 °C, which enhances Na + conductivity.

Topics & Concepts

ChemistryCrystallographyMaterials scienceAnalytical Chemistry (journal)ChromatographyBoron Compounds in ChemistryHydrogen Storage and MaterialsChemical Synthesis and Characterization
Na<sub>2</sub>B<sub>11</sub>H<sub>13</sub> and Na<sub>11</sub>(B<sub>11</sub>H<sub>14</sub>)<sub>3</sub>(B<sub>11</sub>H<sub>13</sub>)<sub>4</sub> as potential solid-state electrolytes for Na-ion batteries | Litcius