Quantifying Sources of Voltage Decay in Long-Term Durability Testing for PEM Water Electrolysis
Elliot Padgett, Haoran Yu, Sarah J. Blair, David A. Cullen, Rajesh Ahluwalia, Deborah J. Myers, Bryan S. Pivovar, Shaun M Alia
Abstract
Meeting a competitive 1$/kg hydrogen cost target for polymer electrolyte membrane water electrolysis (PEMWE) will require advances to significantly reduce capital costs and precious metal catalyst usage, while simultaneously enabling 40,000–80,000 h stack lifetimes under dynamic use conditions. Minimizing cell voltage decay rates is therefore a key goal for PEMWE, although the fundamental processes governing voltage decay are not yet well understood. Here we present a quantitative approach to analyze the contributions to voltage decay in long-term PEMWE testing using polarization curves, impedance spectroscopy, and post-mortem electron microscopy. We apply this approach to analyze a 28 μV h −1 decay rate observed in a 4000 h durability test of a cell using 0.5 mg cm −2 total PGM catalyst loading (0.4 mg Ir cm −2 anode, 0.1 mg Pt cm −2 cathode) and 3 A cm −2 current density. We also analyze a comparative series of 1000 h tests under different conditions. These results provide valuable insights into anode catalyst degradation processes, as well as transferrable methodology for PEMWE durability research.