Influence of Post-Deposition Thermal Treatments on the Morpho-Structural, and Bonding Strength Characteristics of Lithium-Doped Biological-Derived Hydroxyapatite Coatings

Abstract

We report on hydroxyapatite (HA) of biological-origin doped with lithium carbonate (LiC) and lithium phosphate (LiP) coatings synthesized by Pulsed laser deposition onto Ti6Al4V substrates fabricated by the Additive manufacturing technique. A detailed comparison from the structural, morphological, chemical composition, wetting behavior and bonding strength standpoints of as-deposited (NTT) and post-deposition thermal-treated (TT) coatings at temperatures ranging from 400 to 700 °C (i.e., TT400–TT700), was performed. Structural investigations indicated a complete crystallization of the initially amorphous HA-based layers at temperatures in excess of 500 °C. The morphological analyses emphasized the rough appearance of the film surfaces, consisting of particulates whose dimensions increased at higher temperatures, with an emphasis on LiC coatings. AFM investigations evidenced rough surfaces, with a clear tendency to increase in corrugation with the applied temperature, in the case of LiC coatings. A hydrophobic behavior was observed for control, NTT and TT400 samples, whilst a radical shift towards hydrophilicity was demonstrated for both types of structures at higher temperatures. In the case of TT500–TT700 coatings, the pull-out adherence values increased considerably compared to control ones. Taking into consideration the obtained results, the positive influence of post-deposition thermal treatments (performed at higher temperatures) on the physical–chemical and mechanical properties of LiC and LiP coatings was indicated. Alongside these improved characteristics observed at elevated temperatures, the sustainable nature of the used BioHA materials should recommend them as viable alternatives to synthetic HA ones for bone implant applications.

Topics & Concepts