Preparation of SiC <sub>f</sub> /Si–O–C composites by impregnation pyrolysis of polysiloxane and its electromagnetic wave absorption properties
Boying Xing, Donghai Ding, Guoqing Xiao, Ning Yang, Changkun Lei, Jiyuan Luo, Yan Mu, Xiaochuan Chong, Chenxi Jing, Xinya Luo, Hualei Cheng
Abstract
Abstract High‐temperature structural electromagnetic wave (EMW) absorption materials are increasing in demand because they can simultaneously possess the functions of mechanical load‐bearing, heatproof, and EMW absorption. Herein, SiC f /Si–O–C composites were prepared by precursor impregnation pyrolysis using continuous SiC fibers needled felt as reinforcement and polysiloxane as a precursor, respectively. The phase composition, microstructure, complex permittivity, and EMW absorption properties of SiC f /Si–O–C composites after annealing at various temperatures were investigated. The annealing at 1400–1500°C affects positively the EMW absorption performance of the composites, because the β‐SiC microcrystals and SiC nanowires were generated by the activation of carbothermal reduction reaction in the composites, and the aspect ratio of SiC nanowires increased with the rise of temperature. The composites exhibit optimal EMW absorption performance, with the effective absorption bandwidth covering the entire X‐band and the minimum reflection loss (RL min ) of −32.8 dB at 4.0 mm when the annealing temperature is raised to 1500°C. This is because that the impedance matching is improved as the rising of ε ′ and decreasing of ε ″ due to the conversion of free carbon in the composite into SiC nanowires.