Structural stability of <b> <i>β</i> </b>-Ga2O3 under ion irradiation
Alexander Petkov, D. Cherns, Wei‐Ying Chen, Junliang Liu, J. D. Blevins, Vincent Gambin, Meimei Li, Dong Liu, Martin Kuball
Abstract
β-Ga2O3 was suggested to have excellent irradiation hardness which makes β-Ga2O3-based devices extremely attractive for nuclear and space applications. To discern the fundamental nano-scale structural changes with irradiation, an in situ irradiation experiment in a transmission electron microscope was carried out using 400 keV Ar ions of fluences up to 8 × 1015 cm−2 (equivalent to four displacements per atom). Contrary to previous works, which indicate a phase transition of β-Ga2O3 into the κ polymorph, the β-Ga2O3 structure was found to remain intact throughout except for (i) anisotropic lattice distortions, which are most significant at low levels of irradiation, and (ii) the appearance of additional weak reflections above 2 dpa irradiation. The origin of the extra reflections is discussed.