Silver Nanoparticle–PEDOT:PSS Composites as Water-Processable Anodes: Correlation between the Synthetic Parameters and the Optical/Morphological Properties
Stefania Zappia, Marina Alloisio, Julio Cesar Valdivia, Eduardo Arias, Ivana Moggio, Guido Scavia, Silvia Destri
Abstract
The morphological, spectroscopic and rheological properties of silver nanoparticles (AgNPs) synthesized in situ within commercial PEDOT:PSS formulations, labeled PP@NPs, were systematically investigated by varying different synthetic parameters (NaBH4/AgNO3 molar ratio, PEDOT:PSS formulation and silver and PEDOT:PSS concentration in the reaction medium), revealing that only the reagent ratio affected the properties of the resulting nanoparticles. Combining the results obtained from the field-emission scanning electron microscopy analysis and UV-Vis characterization, it could be assumed that PP@NPs’ stabilization occurs by means of PSS chains, preferably outside of the PEDOT:PSS domains with low silver content. Conversely, with high silver content, the particles also formed in PEDOT-rich domains with the consequent perturbation of the polaron absorption features of the conjugated polymer. Atomic force microscopy was used to characterize the films deposited on glass from the particle-containing PEDOT:PSS suspensions. The film with an optimized morphology, obtained from the suspension sample characterized by the lowest silver and NaBH4 content, was used to fabricate a very initial prototype of a water-processable anode in a solar cell prepared with an active layer constituted by the benchmark blend poly(3-hexylthiophene) and [6,6]-Phenyl C61 butyric acid methyl ester (PC60BM) and a low-temperature, not-evaporated cathode (Field’s metal).