Plasma-Induced Catalyst Support Defects for the Photothermal Methanation of Carbon Dioxide
Salina Jantarang, Simone Ligori, Jonathan Horlyck, Emma C. Lovell, Tze Hao Tan, Bingqiao Xie, Rose Amal, Jason Scott
Abstract
The presence of defects in a catalyst support is known to benefit catalytic activity. In this work, a He-plasma treatment-based strategy for introducing and stabilising defects on a Ni/TiO2 catalyst for photothermal CO2 hydrogenation was established. The impact of pretreatment step sequence—which comprised He-plasma treatment and reduction/passivation—on defect generation and stabilisation within the support was evaluated. Characterisation of the Ni/TiO2 catalysts indicated that defects created in the TiO2 support during the initial plasma treatment stage were then stabilised by the reduction/passivation process, (P-R)Ni/TiO2. Conversely, performing reduction/passivation first, (R-P)Ni/TiO2, invoked a resistance to subsequent defect formation upon plasma treatment and consequently, poorer photothermal catalytic activity. The plasma treatment altered the metal-support interaction and ease of catalyst reduction. Under photothermal conditions, (P-R)Ni/TiO2 reached the highest methane production in 75 min, while (R-P)Ni/TiO2 required 165 min. Decoupling the impacts of light and heat indicated thermal dominance of the reaction with CO2 conversion observed from 200 °C onwards. Methane was the primary product with carbon monoxide detected at 350 °C (~2%) and 400 °C (~5%). Overall, the findings demonstrate the importance of pretreatment step sequence when utilising plasma treatment to generate active defect sites in a catalyst support.