Analysis of Photoluminescence and Dosimetric Properties of (Ce, Tb)-codoped Magnesium Orthosilicate Single Crystals
Kensei Ichiba, Yuma Takebuchi, Hiromi Kimura, Takumi Kato, Daisuke Nakauchi, Noriaki Kawaguchi, Takayuki Yanagida
Abstract
In this study, Mg 1.995-x SiO 4 :xCe, 0.005Tb (x = 0 and 0.01) single crystals were synthesized by the floating zone method and their photoluminescence (PL) and dosimetric properties were evaluated.In the PL process, emission peaks due to the 4f-4f transitions of Tb 3+ ions were observed in the x = 0 and 0.01 samples, and the emission peak due to the 5d-4f transitions of Ce 3+ ions was detected in the x = 0.01 sample.In the thermally stimulated luminescence (TSL) process, only emission peaks due to the 4f-4f transitions of Tb 3+ ions were observed in both samples, and the x = 0.01 sample had higher TSL intensity than the x = 0 sample.The x = 0.01 sample showed a lower detection limit of 0.01 mGy and a spatial resolution of 50.0 μm under X-ray irradiation.