Microstructure, high-temperature cyclic oxidation, and hot corrosion behaviors of Inconel 718 alloy produced by laser-induction hybrid cladding
Lei Qin, Pan Ren, Yanliang Yi, Dongchu Chen, Yang Lu, Daxiang Sun, Changliang Shi, Shengfeng Zhou
Abstract
The microstructure evolution, cyclic oxidation, and hot corrosion behavior of the unheated-treated (As-built) and solution + double aging (SDA)-treated Inconel 718 alloys fabricated through laser-induction hybrid cladding (LIHC) were investigated. It was found that the as-built Inconel 718 alloy exhibits a columnar dendritic with intergranular Laves phase. After SDA-treated, γ", γ′, δ and carbide phases precipitated, the Laves phase became fine and dispersed. After cyclic oxidation, the Cr2O3 scales were formed on both as-built and SDA-treated LIHC-produced Inconel 718 alloy, which could provide good cyclic oxidation resistance for the Inconel 718 alloy. However, the as-built and SDA-treated LIHC-produced Inconel 718 alloy suffered severe hot corrosion in 95 wt% Na2SO4 + 5 wt% NaCl mixed salt solution and many corrosion products were generated, including Cr2O3, NiCr2O4, NaNbO3, Na2CrO4, NiFe2O4, Fe3O4, and NiO. Nevertheless, the SDA-treated sample showed better cyclic oxidation and hot corrosion resistance than the as-built sample, owing to the more compact Cr2O3 scale.