Characterization of Trapping Effects Related to Carbon Doping Level in AlGaN Back-Barriers for AlGaN/GaN HEMTs
Ragnar Ferrand-Drake Del Castillo, Ding-Yuan Chen, Jr‐Tai Chen, Mattias Thorsell, Vanya Darakchieva, Niklas Rorsman
Abstract
The impact of different carbon concentrations in the Al <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$_{\text{0}.\text{06}}$</tex-math> </inline-formula> Ga <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$_{\text{0}.\text{94}}$</tex-math> </inline-formula> N graded back-barrier and GaN buffer of high electron mobility transistors (HEMTs) is investigated. Four epi-wafers with different carbon concentrations, ranging from 1 <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$\times$</tex-math> </inline-formula> 10 <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$^{\text{17}}$</tex-math> </inline-formula> to 5 <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$\times$</tex-math> </inline-formula> 10 <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$^{\text{17}}$</tex-math> </inline-formula> cm <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$^{-\text{3}}$</tex-math> </inline-formula> , were grown by metal organic chemical vapor deposition (MOCVD). HEMTs with 100 and 200 nm gate lengths were fabricated and characterized with dc, Pulsed-IV, drain current transient spectroscopy (DCTS), and large-signal measurements at 30 GHz. It is shown that the back-barrier effectively prevents buffer-related electron trapping. The highest C-doping provides the best 2DEG confinement, while lower carbon doping levels are beneficial for a high output power and efficiency. A C-doping of 1 <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$\times$</tex-math> </inline-formula> 10 <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$^{\text{17}}$</tex-math> </inline-formula> cm <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$^{-\text{3}} $</tex-math> </inline-formula> offers the highest output power at maximum power added efficiency (PAE) (1.8 W/mm), whereas 3 <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$\times$</tex-math> </inline-formula> 10 <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$^{\text{17}}$</tex-math> </inline-formula> cm <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$^{-\text{3}}$</tex-math> </inline-formula> doping provides the highest PAE ( <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$>$</tex-math> </inline-formula> 40%). The C-profiles acquired by using secondary ion mass spectroscopy (SIMS), in combination with DCTS, is used to explain the electron trapping effects. Traps associated with the C-doping in the back-barrier are identified and the bias ranges for the trap activation are discussed. The study shows the importance of considering the C-doping level in the back-barrier of microwave GaN HEMTs for power amplification and generation.