Low-Velocity Impact Response on Glass Fiber Reinforced 3D Integrated Woven Spacer Sandwich Composites
Mahfuz Bin Rahman, Lvtao Zhu
Abstract
This study presents an experimental investigation on the low-velocity impact response of three-dimensional integrated woven spacer sandwich composites made of high-performance glass fiber reinforced fabric and epoxy resin. 3D integrated woven spacer sandwich composites with five different specifications were produced using a hand lay-up process and tested under low-velocity impact with energies of 5 J, 10 J, and 15 J. The results revealed that the core pile's heights and diverse impact energies significantly affect the stiffness and energy absorption capacity. There is no significant influence of face sheet thickness on impact response. Moreover, the damage morphologies of 3D integrated woven spacer sandwich composites under different impact energies were analyzed by simple visualization of the specimen. Different damage and failure mechanisms were observed, including barely visible damage, visible damage, and clearly visible damage. Moreover, it was noticed that the damage of 3D integrated woven spacer sandwich composites samples only constraints to the impacted area and does not affect the integrity of the samples.