MOF-Derived Co<sub>3</sub>S<sub>4</sub> Nanoparticles Embedded in Nitrogen-Doped Carbon for Electrochemical Oxygen Production
Nachiketa Sahu, J. N. Behera
Abstract
The development of a simple and effective strategy for designing a highly efficient oxygen evolution electrocatalyst is more important to speed up the efficiency-limiting step involved in water electrolysis. The high efficiency of the oxygen evolution reaction (OER) is directly correlated with the class of electrode materials employed. This work reports a series of Co 3 S 4 nanoparticles (Co 3 S 4 -2h, Co 3 S 4 -3h, and Co 3 S 4 -4h) derived from a metal–organic framework (MOF) via a single-step annealing strategy with varying reaction times for the study of OER. During the annealing process, the MOF precursor [Co 3 (tiron-bpy) 2 (bpy)(H 2 O) 8 ]·(H 2 O) 2 termed as Co-T-BPY directly converted to cobalt sulfide (Co 3 S 4 ) nanoparticles, along with additional support of the N-doped carbon moiety. Interestingly, variation of reaction time in a fixed temperature condition played a decisive role in optimizing the surface area with huge active sites of the derived products. The optimized Co 3 S 4 -3h product needed an overpotential of 285 mV to reach 10 mA cm –2 current density and an acceptable Tafel value (109 mV dec –1 ) with excellent 14 h of stability performance under harsh alkaline conditions. The OER results are attributed to the combined effect of the Co 3 S 4 phase and N-doped carbon matrix, resulting in substantial stability and high conductivity. Therefore, we believe that the time variation strategy for the preparation of a cobalt-based non-precious electrode material can pave the way in search of an OER-efficient electrocatalyst.