High-temperature corrosion mechanism of a promising scandium tantalate ceramic for next generation thermal barrier coating under molten calcium–magnesium-aluminosilicate (CMAS)
Fuxing Ye, Yihui Yuan, Shuai Yan, Lei Guo, Jianxing Yu
Topics & Concepts
Materials scienceCorrosionCoatingMetallurgyScandiumDissolutionCeramicThermal barrier coatingThermal stabilityChemical engineeringComposite materialEngineeringHigh-Temperature Coating BehaviorsAdvanced ceramic materials synthesisNuclear materials and radiation effects