Cooling Performance of a Nano Phase Change Material Emulsions-Based Liquid Cooling Battery Thermal Management System for High-Capacity Square Lithium-Ion Batteries
Guanghui Zhang, Guofeng Chen, Pan Li, Ziyi Xie, Ying Li, Tuantuan Luo
Abstract
This study investigated the application of nanophase change material emulsions (NPCMEs) for thermal management in high-capacity ternary lithium-ion batteries. We formulated an NPCME of n-octadecane (n-OD) and n-eicosane (n-E) with a mass fraction of 10%, whose phase change temperatures are 25.5 °C and 32.5 °C, respectively, with specific heat capacities 2.1 and 2.4 times greater than water. Experiments were conducted to evaluate the thermal control performance and latent heat utilization efficiency of these NPCMEs. The NPCMEs with an n-OD mass fraction of 10% (NPCME-n-OD), particularly reduced the battery pack’s maximum temperature and temperature difference to 41.6 °C and 3.72 °C under a 2 C discharge rate, lower than the water-cooled group by 1.3 °C and 0.3 °C. This suggests that nano emulsions with phase change temperatures close to ambient temperatures exhibit superior cooling performance. Increased flow rates from 50 mL/min to 75 mL/min significantly lowered temperatures, resulting in temperature reductions of 2.73 °C for the NPCME-n-OD group and 3.37 °C for the NPCME-n-E group. However, the latent heat utilization efficiency of the nano emulsions decreased, leading to increased system energy consumption. Also, it was found that the inlet temperature of the NPCMEs was very important for good thermal management. The right inlet temperatures make it easier to use phase change latent heat, while excessively high temperatures may make thermal management less effective.