Cytotoxicity, inflammation, biomineralization, and immunoexpression of IL-1β and TNF-α promoted by a new bioceramic cement
Leopoldo Cosme‐Silva, Amanda Ferreira dos Santos, Camila Soares Lopes, Renan Dal‐Fabbro, Francine Benetti, João Eduardo Gomes‐Filho, Índia Olinta de Azevedo Queiroz, Edílson Ervolino, Naiana Viana Viola
Abstract
Aim To evaluate the cytotoxicity, biocompatibility and mineralization capacity of BIO-C PULPO, and MTA. Methodology L929 fibroblasts were cultured and MTT assay was used to determine the material cytotoxicity on 6, 24, and 48 h. A total of 30 male rats (Wistar) aged between 4 and 6 months, weighing between 250 and 300 g were used. Polyethylene tubes containing BIO-C PULPO, MTA, and empty tubes were implanted into dorsal connective tissue. After the experimental periods (7, 15, 30, 60, and 90 days) the tubes were histologically analyzed using hematoxylin-eosin (H&E), immunolabeling of IL-1β and TNF-α, and von Kossa staining, or without staining for polarized light analysis. The average number of inflammatory cells was quantified; the mineralization assessment was determined by the area marked in μm2 and semiquantitative immunolabeling analyses of IL-1β and TNF-α were performed. Then, data underwent statistical analysis with a 5% significance level. Results It was observed that BIO-C PULPO and MTA presented cytocompatibility at 6, 24, and 48 similar or higher than control for all evaluated period. On periods 7 and 15 days, BIO-C PULPO was the material with the highest number of inflammatory cells (p<0.05). On periods 30, 60, and 90 days, BIO-C PULPO and MTA presented similar inflammatory reactions (p>0.05). No statistical differences were found between Control, BIO-C PULPO, and MTA for immunolabeling of IL-1β and TNF-α in the different periods of analysis (p<0.05). Positive von Kossa staining and birefringent structures under polarized light were observed in all analyzed periods in contact with both materials, but larger mineralization area was found with BIO-C PULPO on day 90 (p<0.05). Conclusion BIO-C PULPO was biocompatible and induced mineralization similar to MTA.