Low Specific Contact Resistivity of 10<sup>−3</sup>Ω·cm<sup>2</sup> for Ti/Al/Ni/Au Multilayer Metals on SI-GaN:Fe Substrate
Xianghong Yang, Long Hu, Xin Dang, Xin Li, Weihua Liu, Chuanyu Han, Li Song
Abstract
For the application of third-generation compound semiconductors based on high-voltage, high-power, and high-frequency devices, particularly in photoconductive semiconductor switches (PCSSs), the ohmic contact preparation technology on semi-insulating substrates is crucial. However, iron-doped semi-insulating gallium nitride (SI-GaN:Fe) with low carrier concentration and high bulk resistivity has a very difficult time achieving good ohmic contact characteristics. Here, we have demonstrated preliminary results on an interesting class of good ohmic contact of Ti/Al/Ni/Au on Ga-face of SI-GaN:Fe. The results indicated that the Ti and Al thickness ratio is a critical parameter when determining the optimum annealing temperature and time for ohmic contact. With alloyed Ti/Al/Ni/Au stacks of 20 nm/120 nm/55 nm/45 nm on SI-GaN:Fe after annealing at 850 °C for 35 s in N2 atmosphere, a low specific contact resistivity of <inline-formula xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> <tex-math notation="LaTeX">$10^{-3}\,\,\Omega \cdot $ </tex-math></inline-formula> cm2 is achieved. At a future date, such excellent ohmic contact characteristics can be applied to the SI-GaN:Fe-based high-power PCSS.