Influence of WC-Co hard metal microstructure on defect density, initiation and propagation kinetics of fatigue cracks starting at intrinsic and artificial defects under a negative stress ratio

Thomas Klünsner, Tanja Lube, C. L. Gettinger, Lukas Walch, Reinhard Pıppan

2020Acta Materialia35 citationsDOI

Topics & Concepts

Materials scienceMicrostructureNucleationGrain sizeComposite materialBendingWeibull distributionStress (linguistics)Crystallographic defectCyclic stressFatigue limitKineticsThermodynamicsCrystallographyQuantum mechanicsPhilosophyLinguisticsMathematicsStatisticsChemistryPhysicsAdvanced materials and compositesTunneling and Rock MechanicsMetal Alloys Wear and Properties