High temperature corrosion of (Er0.25Tm0.25Yb0.25Lu0.25)2Si2O7 environmental barrier coating material subjected to water vapor and molten calcium–magnesium–aluminosilicate (CMAS)
Luchao Sun, Yixiu Luo, Zhilin Tian, Tiefeng Du, Xiaomin Ren, Jialin Li, Wanpeng Hu, Jie Zhang, Jingyang Wang
Topics & Concepts
CorrosionMaterials scienceAluminosilicateWater vaporDurabilityCoatingCombustionThermal barrier coatingCompatibility (geochemistry)Calcium aluminosilicateMetallurgyComposite materialChemistryBiochemistryOrganic chemistryCatalysisAdvanced ceramic materials synthesisNuclear materials and radiation effectsMicrowave Dielectric Ceramics Synthesis