Kinetically Stable Oxide Overlayers on Mo<sub>3</sub>P Nanoparticles Enabling Lithium–Air Batteries with Low Overpotentials and Long Cycle Life
Alireza Kondori, Zhen Jiang, Mohammadreza Esmaeilirad, Mahmoud Tamadoni Saray, Arvin Kakekhani, Kamil Küçük, Pablo Navarro Munoz Delgado, Sadaf Maghsoudipour, John Hayes, Christopher S. Johnson, Carlo U. Segre, Reza Shahbazian‐Yassar, Andrew M. Rappe, Mohammad Asadi
Abstract
Abstract The main drawbacks of today's state‐of‐the‐art lithium–air (Li–air) batteries are their low energy efficiency and limited cycle life due to the lack of earth‐abundant cathode catalysts that can drive both oxygen reduction and evolution reactions (ORR and OER) at high rates at thermodynamic potentials. Here, inexpensive trimolybdenum phosphide (Mo 3 P) nanoparticles with an exceptional activity—ORR and OER current densities of 7.21 and 6.85 mA cm −2 at 2.0 and 4.2 V versus Li/Li + , respectively—in an oxygen‐saturated non‐aqueous electrolyte are reported. The Tafel plots indicate remarkably low charge transfer resistance—Tafel slopes of 35 and 38 mV dec −1 for ORR and OER, respectively—resulting in the lowest ORR overpotential of 4.0 mV and OER overpotential of 5.1 mV reported to date. Using this catalyst, a Li–air battery cell with low discharge and charge overpotentials of 80 and 270 mV, respectively, and high energy efficiency of 90.2% in the first cycle is demonstrated. A long cycle life of 1200 is also achieved for this cell. Density functional theory calculations of ORR and OER on Mo 3 P (110) reveal that an oxide overlayer formed on the surface gives rise to the observed high ORR and OER electrocatalytic activity and small discharge/charge overpotentials.