The effect of different brines and temperatures on the competitive degradation mechanisms of CO2 and H2S in API X65 carbon steel

Bernardo Augusto Farah Santos, Rhuãn Costa Souza, Maria Eduarda Dias Serenário, M.C. Gonçalves, E.P. Mendes Júnior, Thiago A. Simões, Jefferson Rodrigues de Oliveira, Gustavo L. Vaz, Lecino Caldeira, José Antônio da Cunha Ponciano Gomes, Alysson Helton Santos Bueno

2020Journal of Natural Gas Science and Engineering27 citationsDOI

Topics & Concepts

MackinawitePyriteThiosulfateCorrosionChlorideScanning electron microscopeSulfideDielectric spectroscopyMaterials scienceSodium thiosulfateCarbon steelElectrochemistrySodiumBrineHydrogen sulfideChemistryInorganic chemistryChemical engineeringMetallurgyComposite materialElectrodeSulfurOrganic chemistryPhysical chemistryEngineeringCorrosion Behavior and InhibitionConcrete Corrosion and DurabilityHydrogen embrittlement and corrosion behaviors in metals
The effect of different brines and temperatures on the competitive degradation mechanisms of CO2 and H2S in API X65 carbon steel | Litcius