Hydrogen permeation in X80 steel during corrosion induced by the synergistic effects of sulfate-reducing bacteria and alternating current
Mengdi Yan, Boxin Wei, Jin Xu, Changkun Yu, Cheng Sun
Topics & Concepts
Sulfate-reducing bacteriaPermeationCorrosionCurrent (fluid)HydrogenChemistryAlternating currentMetallurgyMaterials scienceSulfateInorganic chemistryChemical engineeringNuclear chemistryMembraneBiochemistryOrganic chemistryThermodynamicsEngineeringPower (physics)PhysicsHydrogen embrittlement and corrosion behaviors in metalsCorrosion Behavior and InhibitionConcrete Corrosion and Durability