Investigation of the effect of NiCrAlY/Cr<SUB align="right">2O<SUB align="right">3/YSZ plasma coatings on erosion performance of MDN 420 steel at high temperature
G. Madhu Sudana Reddy, C. Durga Prasad, Pradeep M. Patil, Gagan Shetty, Naresh Kakur, М. Р. Рамеш
Abstract
The purpose of the current study was to use an air jet erosion tester to examine the erosive behaviour of plasma sprayed coatings on MDN-420 that were composed of 70% NiCrAlY, 25% Cr2O3, and 5% YSZ. Microstructure and phase studies were performed. Measurements were made on the microhardness and adhesion strength. Al2O3 erodent was used in a solid particle erosion test with impact angles of 30° and 90° at 300°C, 500°C, and 700°C. The erosion volume loss was measured using an optical profilometer. For the test temperature used, it was found that the coating's erosion resistance was greater than that of the substrate and that it was more pronounced at higher impact angles and higher temperatures. The shape of the degraded coating surface reflects the coating's ductile nature.