Nonconductive Metal Oxide Gas Diffusion Layer for Mitigating Electrowetting during CO<sub>2</sub> Electrolysis
Robert Haaring, Phil Woong Kang, Jae Wook Lee, Junpyo Lee, Hyunjoo Lee
Abstract
Gas diffusion electrodes (GDEs) are extensively used for high current density electrochemical CO 2 electrolysis (ECO 2 R), enabled by significantly reducing mass transfer resistance of CO 2 to the catalyst layer. Conventionally, these GDEs are based upon hydrophobic carbon-based gas-diffusion layers (GDLs) that facilitate the gas transport; however, these supports are prone to flood with electrolyte during electrolysis. This potential-induced flooding, known as electrowetting, is related to the inherent conductivity of carbon and limits the activity of ECO 2 R. To investigate the effect of electrical conductivity more carefully, a GDE is constructed based on a Cu mesh with a nonconductive microporous GDL applied to this substrate, the latter composed of a mixture of metal oxide and polytetrafluoroethylene. With alumina as the metal oxide, a stable operation is obtained at −200 mA cm –2 with 70% selectivity for ECO 2 R (with over half toward C 2+ products) without flooding as observed by in situ microscopy. On the contrary, with a Vulcan carbon-based GDL, the initial activity is rapidly lost as severe flooding ensues. It is reasoned that electrowetting is averted by virtue of the nonconductive nature of alumina, providing a new perspective on alternative GDL compositions and their influence on ECO 2 R performance.