Regulating Metal Centers of MOF-74 Promotes PEO-Based Electrolytes for All-Solid-State Lithium-Metal Batteries
Jiaxin Wu, Yuhan Ma, Haichang Zhang, Haonan Xie, Jin Hu, Chunsheng Shi, Biao Chen, Chunnian He, Naiqin Zhao
Abstract
Poly(ethylene oxide) (PEO)-based electrolytes have been extensively studied for all-solid-state lithium-metal batteries due to their excellent film-forming capabilities and low cost. However, the limited ionic conductivity and poor mechanical strength of the PEO-based electrolytes cannot prevent the growth of undesirable lithium dendrites, leading to the failure of batteries. Metal–organic frameworks (MOFs) are functional materials with a periodic porous structure that can improve the electrochemical performance of PEO-based electrolytes. However, the enhancement effect of MOFs with different metal centers and the interaction mechanism with PEO remain unclear. Herein, MOF-74s with Cu or Ni centers are prepared and used as fillers of PEO-based electrolytes. Adding 15 wt % of Cu-MOF-74 to the PEO-based electrolyte (15%Cu-MOF/P–Li) effectively improves the ionic conductivity, lithium transference number, and mechanical strength of the PEO-based electrolyte simultaneously. Furthermore, the ordered pore channels of Cu-MOF-74 provide uniform Li-ion transport pathways, facilitating homogeneous Li + deposition. As a result, the lithium symmetric cell with 15%Cu-MOF/P–Li shows stable cycles for 1080 h at 0.1 mA cm –2 and 0.1 mAh cm –2, and the Li | 15% Cu-MOF/P–Li | LFP full cell exhibits a long cycle life up to 200 cycles at 60 °C and 0.5 C, with a capacity retention rate of 89.7%.