Damage causes and failure analysis of a steam turbine blade made of martensitic stainless steel after 72,000 h of working
A. Rivaz, S.H. Mousavi Anijdan, Mohammad Moazami-Goudarzi, A.Nazari Ghohroudi, H.R. Jafarian
Topics & Concepts
Materials scienceTurbine bladeMartensiteCorrosionMetallurgyMartensitic stainless steelOptical microscopeSteam turbineBlade (archaeology)AlloyEnergy-dispersive X-ray spectroscopyService lifeBrittlenessFatigue limitScanning electron microscopeTurbineComposite materialMicrostructureStructural engineeringMechanical engineeringEngineeringHigh Temperature Alloys and CreepMetal Alloys Wear and PropertiesHigh-Temperature Coating Behaviors