Piezoresistive Properties of 3D-Printed Polylactic Acid (PLA) Nanocomposites
Razieh Hashemi Sanatgar, Aurélie Cayla, Jinping Guan, Guoqiang Chen, Vincent Nierstrasz, Christine Campagne
Abstract
An increasing interest is focused on the application of 3D printing for sensor manufacturing. Using 3D printing technology offers a new approach to the fabrication of sensors that are both geometrically and functionally complex. This work presents the analysis of the 3D-printed thermoplastic nanocomposites compress under the applied force. The response for the corresponding resistance changes versus applied load is obtained to evaluate the effectiveness of the printed layer as a pressure/force sensor. Multi-walled carbon nanotubes (MWNT) and high-structured carbon black (Ketjenblack) (KB) in the polylactic acid (PLA) matrix were extruded to develop 3D-printable filaments. The electrical and piezoresistive behaviors of the created 3D-printed layers were investigated. The percolation threshold of MWNT and KB 3D-printed layers are 1 wt.% and 4 wt.%, respectively. The PLA/1 wt.% MWNT 3D-printed layers with 1 mm thickness exhibit a negative pressure coefficient (NPC) characterized by a decrease of about one decade in resistance with increasing compressive loadings up to 18 N with a maximum strain up to about 16%. In the cyclic mode with a 1 N/min force rate, the PLA/1 wt.% MWNT 3D-printed layers showed good performance with the piezoresistive coefficient or gauge factor (G) of 7.6 obtained with the amplitude of the piezoresistive response (Ar) of about -0.8. KB composites could not show stable piezoresistive responses in a cyclic mode. However, under high force rate compression, the PLA/4 wt.% KB 3D-printed layers led to responses of large sensitivity (Ar = −0.90) and were exempt from noise with a high value of G = 47.6 in the first cycle, which is a highly efficient piezoresistive behavior.