Improved oxidation and ablation resistance of SiCf/SiC-HfB2 composites: Role of oxygen-blocking scale and protection mechanism
Ruru Guo, Lu Li, Zhijian Li, Ruixiao Zheng, Chaoli Ma
Abstract
To improve the oxidation and ablation resistance of SiC f /SiC composites, the as-synthesized ultrafine HfB 2 powder was used as the modification phase to fabricate SiC f /SiC-HfB 2 composites, and their oxidation and ablation behaviors were investigated. Compared with the unmodified SiC f /SiC composites, the oxidation resistance at 800–1500 °C and the ultra-high temperature ablation resistance of SiC f /SiC-HfB 2 composites were significantly improved. After oxidation, a compact compound glass scale consisting of HfO 2 , HfSiO 4 and Si-Hf-O glass was formed, providing the effective oxidation protection. A dual-phase oxide scale composed of HfO 2 skeleton and Si-Hf-O glass was formed after ablation, exhibiting the high viscosity, the significant oxygen-blocking effect and resistance to gas flow scouring. The improved oxidation and ablation resistance of SiC f /SiC-HfB 2 composites could be attributed to the effective protective role of oxygen-blocking scales formed during the oxidation and ablation processes .