Comparative study on hydrogen induced cracking sensitivity of two commercial API 5L X80 steels
Yunying Xing, Zhile Yang, Xingcheng Yao, Xiuyun Wang, Minxu Lu, Lei Zhang, Lijie Qiao
Topics & Concepts
Electron backscatter diffractionMaterials scienceMicrostructureScanning electron microscopeMetallurgyIntergranular corrosionHydrogenTransmission electron microscopyCrackingGrain boundaryOptical microscopeComposite materialChemistryNanotechnologyOrganic chemistryHydrogen embrittlement and corrosion behaviors in metalsCorrosion Behavior and InhibitionNon-Destructive Testing Techniques