Investigation of the irradiation effects in additively manufactured 316L steel resulting in decreased irradiation assisted stress corrosion cracking susceptibility
Michael D McMurtrey, Cheng Sun, Ryann E. Rupp, Ching-Heng Shiau, Rigel D. Hanbury, Nathan Jerred, Robert C. O’Brien
Topics & Concepts
Materials scienceIrradiationStress corrosion crackingUltimate tensile strengthScanning electron microscopeMetallurgyDeformation (meteorology)Composite materialCrackingCorrosionTransmission electron microscopyStress (linguistics)NanotechnologyPhysicsPhilosophyNuclear physicsLinguisticsNuclear Materials and PropertiesAdditive Manufacturing Materials and ProcessesFusion materials and technologies