Crystal transition and thermal behavior of Nylon 12
Ning Ma, Wentao Liu, Lili Ma, Suqin He, Hao Liu, Zhenya Zhang, Aihua Sun, Miaoming Huang, Chengshen Zhu
Abstract
Abstract The polyamide 12 (PA12) with different crystal forms is prepared with three crystallization paths. The crystal structures and corresponding thermal properties are systematically investigated. The results reveal that an α-form and a mixed (α + γ)-form of PA12 can be obtained by casting at 30°C and (40–80°C), respectively. Meanwhile, the γ-form of PA12 can be obtained by both casting at 90°C and slow melt cooling. However, the γ′-form is obtained only by melt quenching. Both the γ and γ′ forms of PA12 exhibit a single melting peak, whereas the α-form exhibits two melting peaks. The higher peak is attributed to the melting of γ-PA12, which originates from the melting–recrystallization of the α-PA12. It is found that the tensile properties of PA12 depend on the crystal forms. Both the γ and γ′-PA12 are strong and tough polymer materials, while α-PA12 is a strong but brittle polymer material.