Modeling the transition from ductile to brittle fracture induced by hydrogen-assisted mechanical degradation in quenching and partitioning (Q&P) steel
Geonjin Shin, Jinheung Park, Sang Yoon Song, Ki-Jung Kim, Hye-Jin Kim, Seok Su Sohn, Myoung‐Gyu Lee
Topics & Concepts
Quenching (fluorescence)Materials scienceDegradation (telecommunications)BrittlenessHydrogenBrittle fractureFracture (geology)MetallurgyComposite materialStructural engineeringForensic engineeringChemistryEngineeringElectrical engineeringPhysicsFluorescenceQuantum mechanicsOrganic chemistryHydrogen embrittlement and corrosion behaviors in metalsMicrostructure and Mechanical Properties of SteelsWelding Techniques and Residual Stresses