Effect of W Content on Microstructure and Properties of Laser Cladding CoCrFeNi HEA Coating
Fangyan Luo, Tuchuan Yang, Yang Zhao, Zhengye Xiong, Jiang Huang
Abstract
The 316L SS surfaces were prepared with CoCrFeNi HEA/W-composite coatings using the laser cladding technique with various mass fractions of W. The mass fractions of W were 10, 20, 30, and 40%. The microstructure of the HEA/W-composite coatings was investigated using a variety of characterization methods. According to the results, the samples were in the BBC phase. In the SEM images, a solid–liquid bonding layer was observed, which indicates the samples had good metallurgical bonding. The W particles prevented the orderly growth of the HEA grains, and a significant refinement of the grains around the W particles occurred. The lattice constants measured by XRD mapping indicate that adding W particles to CoCrFeNi HEA leads to lattice distortion. The hardness of the HEA/W coatings was substantially higher than the substrate and the pure CoCrFeNi coating by hardness measurements and was greatest at a W content of 40%. The hardness of the HEA/W coatings was significantly increased compared to the substrate and the pure CoCrFeNi coating by hardness measurements and was greatest at a W content of 40%. The HEA/W coating was tested for electrochemical corrosion, and a 10% mass fraction of W achieved the highest level of corrosion resistance.