Synthesis and Characterization of Polydimethylsiloxane (PDMS) with Medium Viscosity via Ring-Opening Polymerization
Soni Setiadji, Zulfi Mofa Agasa, Diba Grace Auliya, Fitrilawati Fitrilawati, Norman Syakir, Atiek Rostika Noviyanti, Iman Rahayu, Asep Supriadin, Risdiana Risdiana
Abstract
Duration of use and injectability are external factors for Polydimethylsiloxane (PDMS) that needs to be considered when PDMS utilized as a vitreous substituted liquid in vitreoretinal surgery. In general, PDMS which has been used as a substitute for vitreous humour is PDMS with a low viscosity in the value about 1000 cSt and a high viscosity at a value of about 5000 cSt. Various deficiencies have been encountered from low and high viscosity of PDMS, causing research to be continued to obtain PDMS which has suitable properties as a substitute for vitreous humour. One of them is research to obtain medium viscosity of PDMS with a viscosity value of about 2000 cSt. Here, we reported synthesis and characterization of PDMS with medium viscosity in ranges from 1800 to 2600 mPas. PDMS was synthesized through Ring-Opening Polymerization (ROP) pathway using the monomer of Octamethylcyclotetrasiloxane (D4) and the chain terminator of Hexamethyldisiloxane (MM). Various concentrations of potassium hydroxide (KOH) of 3, 4, 6 and 8 %(w/v) were applied as initiator to form gel of PDMS. All synthesized PDMS samples were identified to have viscosity values of 1800-2600 mPas, refractive index values of 1.4042-1.4044 and surface tension values of 22-23 mN/m. Meanwhile, the results of Fourier-Transform Infrared (FTIR) measurement showed that the absorption peaks were similar to that of our previous report.