Incorporation of 2D-biotene to polyethersulfone ultrafiltration membrane with superhydrophilicity and antifouling properties for removal of organic pollutants
Mahsa Haddad Irani-nezhad, Alireza Khataee, Vahid Vatanpoor, Samira Arefi-Oskoui, Yasin Orooji
Abstract
Here, for the first time, one or few-layer exfoliated 2D-Biotene (E-BIT) was prepared by a cost-effective liquid-phase exfoliation of economical and accessible bulk biotite (B-BIT). The successful preparation of E-BIT was further verified by different characterization methods. XRD pattern demonstrated that B-BIT's basal spacing was increased from 10.07 Å to 11.02 Å. Also, the transparency of the E-BIT to the electron beam showed its small thickness after exfoliation, which was confirmed by AFM results, too. This natural material was utilized as an efficient nano-additive to improve the properties of polyethersulfone (PES) polymeric membrane . E-BIT blended membranes with various quantities (0–2 wt%) were prepared via the non-solvent induced phase inversion method. Small holes at the up layer, coarse finger-like holes and macro-voids at the sublayer were seen in asymmetric prepared membranes. Modification caused the improvement of the membranes' hydrophilicity , which the contact angle was reduced from 69.3 to 53.4 for bare PES and 1 wt% E-BIT blended membranes, respectively. 1 wt% E-BIT blended membrane illustrated flux enhancement of 198.8 L/m 2 h, and high elimination efficiency of bovine serum albumin (99%), reactive red 195 (97.8%), reactive green 9 (93.5%), and reactive blue 19 (88.4%), with improved flux recovery ratio of 73%.