Processing strategy for high strength Ni-based hybrid composite clad on SS 316L steel through microwave heating
Sarbjeet Kaushal, Satnam Singh, Dheeraj Gupta
Abstract
Processing of nickel-based high strength composites and alloys is a difficult and thought-provoking task. In this work, a strategy of heating through microwaves radiation is utilized to process the high strength hybrid Ni-based composite clad on SS 316L steel surface containing 15% (WC-8Co) and 5% Mo. The premixed composite powder was placed on the steel surface and irradiated with domestic microwave applicator having 2.45 GHz fixed frequency and 900 W power. The hybrid clad was successfully developed within 12–15 min of microwave exposure. The processed clad was subjected to various metallurgical and mechanical characterizations to understand the microstructures and phase changes. Microstructural analysis study revealed that the clad of ∼0.85 mm thickness was obtained and presence of dispersed reinforced particles of WC-8Co and Mo in nickel matrix were observed. Some inter-metallic phases of W 2 C, Ni 2 Mo 4 C, Ni 4 W and NiSi 2 were observed in the clad. The average microhardness of the composite clad was712 ± 58 HV. The microwave processed clad exhibited a flexural strength of 852 ± 6 MPa with deformation index of 35 × 10 −5 mm/N. Further, the sliding wear study revealed that the sliding velocity of 1.0 m/s favoured the formation of oxide tribo layers. The various mechanisms of wear revealed by the analysis of worn-out surfaces were abrasion, adhesion, surface pull-out and deformation of surfaces. The microwave processed clad revealed significant improvement in wear resistance in comparison to the steel substrate.