Preparation and Properties of Straw/PLA Wood Plastic Composites for 3D Printing
Jie Jiang, Hai Gu, Bin Li, Jie Zhang
Abstract
Abstract Based on the single screw extruder, straw/PLA composites with different straw mass fraction, drawing temperature and screw speed were prepared with corn straw powder and PLA particles as raw materials, and FDM printing test was carried out to further study the influence of straw mass fraction, drawing temperature and screw speed on the mechanical properties of straw/PLA composites The results show that the tensile strength of the composite is the best when the straw content is 15%, the drawing temperature is 215°C, the screw speed is 60r/min; the flexural strength of the composite is the best when the straw content is 15%, the drawing temperature is 215°C, the screw speed is 70r/min; the hardness of the composite is the best when the straw content is 10%, the drawing temperature is 195°C, the screw speed is 70r/min.