Fracture Resistance Analysis of CAD/CAM Interim Fixed Prosthodontic Materials: PMMA, Graphene, Acetal Resin and Polysulfone
Cristian Abad‐Coronel, Carolina Calle, Gabriela Abril, César A. Paltán, Jorge I. Fajardo
Abstract
The aim of this study was to evaluate and compare the fracture resistance of temporary restorations made of polymethylmethacrylate (PMMA), graphene-modified PMMA (GRA), acetal resin (AR) and polysulfone (PS) obtained by a subtractive technique (milling) using a computer-aided design and manufacturing (CAD/CAM) system of a three-unit fixed dental prosthesis (FDP). METHODS: Four groups of ten samples were fabricated for each material. Each specimen was characterized by a compression test on a universal testing machine, all specimens were loaded to fracture and the value in Newtons (N) was recorded by software connected to the testing machine. The fracture mode was evaluated on all samples using a stereomicroscope. RESULTS: value < 0.005) between PMMA and the other three materials (PMMA: 1302.71 N; GRA: 1990.02 N; RA: 1796.20 N; PS: 2234.97). PMMA presented a significantly lower value than the other materials, and PS showed the highest value. GRA and RA presented a similar range of values but they were still higher than those of PMMA. CONCLUSIONS: GRA, RA and PS are presented as valid options within the range of interim milled restorative materials and as alternatives to PMMA.