Nickel vanadate nitrogen-doped carbon nanocomposites for high-performance supercapacitor electrode

Abstract

A nickel-vanadium-based bimetallic precursor was produced using the polymerization process by urea-formaldehyde copolymers. The precursor was then calcined at 800 °C in an argon ambiance to form a Ni 3 V 2 O 8 -NC magnetic nanocomposite. Powerful techniques were used to study the physical characteristics and chemical composition of the fabricated Ni 3 V 2 O 8 -NC electrode. PXRD, Raman, and FTIR analyses proved that the crystal structure of Ni 3 V 2 O 8 -NC included N-doped graphitic carbon. FESEM and TEM analyses imaging showed the distribution of the Ni 3 V 2 O 8 nanoparticles on the layered graphitic carbon structure. TEM images showed the prepared sample has a particle size of around 10–15 nm with an enhanced active site area of 146 m 2 /g, as demonstrated by BET analysis. Ni 3 V 2 O 8 -NC nanocomposite exhibits magnetic behaviors and a magnetization saturation value of 35.99 emu/g. The electrochemical (EC) studies of the synthesized Ni 3 V 2 O 8 -NC electrode proceeded in an EC workstation of three-electrode. In a 5 M potassium hydroxide as an electrolyte, the cyclic voltmeter exhibited an enhanced capacitance ( C S ) of 915 F/g at 50 mV/s. Galvanic charge-discharge (GCD) study also exhibited a superior capacitive improvement of 1045 F/g at a current density ( I t ) of 10 A/g. Moreover, the fabricated Ni 3 V 2 O 8 -NC nanocomposite displays a good power density ( P t ) of 356.67 W/kg, improved ion accessibility, and substantial charge storage. At the high energy density ( E t ) of 67.34 W h/kg, the obtained P t was 285.17 W/kg. The enhanced GCD rate, cycle stability, and E t of the Ni 3 V 2 O 8 -NC magnetic nanocomposite nominate the sample as an excellent supercapacitor electrode. This study paves the way for developing effective, efficient, affordable, and ecologically friendly electrode materials.

Topics & Concepts